CONDUCTIVE MATERIAL :

• Aluminium Barrel - 99.6%
• Copper Palm - 99.95%
• Final Metal State - Fully Annealed, Including Joint
• Joining Method - Friction Welding
• Finish - Natural

CONDUCTIVITY

• Aluminium - 61.8% IACS (MIN)
• Copper - 99.7% IACS

RANGE : 25 mm2 to 800 mm2

Aluminium barrel, electrical cable lugs, electrical cable connectors, bimetal connectors, bimetallic lugs, cable connectors are chemically treated to reduce contact resistance and corrosion and are filled electrically conductive corrosion inhabitant with a jointing compound and capped

CONDUCTIVE MATERIAL :

• Aluminium Barrel - 99.6%
• Copper Palm - 99.95%
• Final Metal State - Fully Annealed, Including Joint
• Joining Method - Friction Welding
• Finish - Natural

CONDUCTIVITY

• Aluminium - 61.8% IACS (MIN)
• Copper - 99.7% IACS

ALUMINIUM RANGE : 50 mm2 to 240 mm2
COPPER RANGE : 16 mm2 to 240 mm2

Aluminium Barrel, electrical cable lugs, electrical cable connectors, bimetal connectors, bimetallic lugs, cable connectors are chemically treated to reduce contact resistance and corrosion and are filled electrically conductive corrosion inhabitant with a jointing compound and capped

CONDUCTIVE MATERIAL :

• Aluminium Barrel - 99.6%
• Copper Palm - 99.95%
• Final Metal State - Fully Annealed, Including Joint
• Joining Method - Friction Welding
• Finish - Natural

CONDUCTIVITY

• Aluminium - 61.8% IACS (MIN)
• Copper - 99.7% IACS

ALUMINIUM RANGE : 16 mm2 to 300 mm2
COPPER RANGE : 10 mm2 to 240 mm2

Aluminium Barrel, electrical cable lugs, electrical cable connectors, bimetal connectors, bimetallic lugs, cable connectors are chemically treated to reduce contact resistance and corrosion and are filled electrically conductive corrosion inhabitant with a jointing compound and capped

CONDUCTIVE MATERIAL :

• Aluminium Barrel - 99.6%
• Copper Palm - 99.95%
• Final Metal State - Fully Annealed, Including Joint
• Joining Method - Friction Welding
• Finish - Natural

CONDUCTIVITY

• Aluminium - 61.8% IACS (MIN)
• Copper - 99.7% IACS

ALUMINIUM RANGE : 6 mm2 to 630 mm2

Aluminium Barrel are chemically treated to reduce contact resistance and corrosion and are filled electrically conductive corrosion inhabitant with a jointing compound and capped

CONDUCTIVE MATERIAL :

• Aluminium Barrel - 99.6%
• Copper Palm - 99.95%
• Final Metal State - Fully Annealed, Including Joint
• Joining Method - Friction Welding
• Finish - Natural

CONDUCTIVITY

• Aluminium - 61.8% IACS (MIN)
• Copper - 99.7% IACS